Abstract
In this paper, we propose a high-performance separative extended gate ion-sensitive field-effect transistor (SEGISFET) that consists of a tin dioxide (SnO2) SEG sensing part and a double-gate structure amorphous indium gallium zinc oxide (a-IGZO) thin-film transistor (TFT) with tantalum pentoxide/silicon dioxide (Ta2O5/SiO2)-engineered top-gate oxide. To increase sensitivity, we maximized the capacitive coupling ratio by applying high-k dielectric at the top-gate oxide layer. As an engineered top-gate oxide, a stack of 25 nm-thick Ta2O5 and 10 nm-thick SiO2 layers was found to simultaneously satisfy a small equivalent oxide thickness (∼17.14 nm), a low leakage current, and a stable interfacial property. The threshold-voltage instability, which is a fundamental issue in a-IGZO TFTs, was improved by low-temperature post-deposition annealing (∼87 °C) using microwave irradiation. The double-gate structure a-IGZO TFTs with engineered top-gate oxide exhibited high mobility, small subthreshold swing, high drive current, and larger on/off current ratio. The a-IGZO SEGISFETs with a dual-gate sensing mode showed a pH sensitivity of 649.04 mV pH−1, which is far beyond the Nernst limit. The non-ideal behavior of ISFETs, hysteresis, and drift effect also improved. These results show that the double-gate structure a-IGZO TFTs with engineered top-gate oxide can be a good candidate for cheap and disposable SEGISFET sensors.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.