Abstract
We report the fabrication and electrical characteristics of high-performance amorphous indium gallium zinc oxide (a-IGZO) thin-film transistors (TFTs) with a polymer gate dielectric prepared by spin coating on a glass substrate at different oxygen partial pressure values. The transmittance of the deposited polymer film was greater than 90% at 600 nm a-IGZO thin films were deposited on glass substrates using RF magnetron sputtering at different oxygen partial pressure values. The a-IGZO TFTs were prepared by rapid thermal annealing at 350 °C for 10 min at a 0.2% oxygen partial pressure. It was observed that a-IGZO TFTs with an active channel layer exhibited enhanced mode operation, a threshold voltage of 1 V, an on-off current ratio of 10 3, and a field-effect mobility of 18 cm 2/Vs.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.