Abstract
In this study, NiAl-34Cr and NiAl-28Cr-6Mo eutectic alloys were produced by electric current assisted sintering (ECAS) method in a 3500-4200 A current range with a waiting time of 47 minutes. Phase examinations of the obtained samples were carried out with the help of X-ray diffraction analysis (XRD). While determining NiAl and Cr phases in NiAl-34Cr alloy from XRD patterns; It was determined that NiAl-28Cr-6Mo alloy consists of two phases, together with Mo residues, NiAl and CrMo. According to the Archimed principle, the relative density of NiAl-34Cr and NiAl-28Cr-6Mo alloys was determined as 96.2%, 97.9% respectively. The hardness values of NiAl-34Cr and NiAl-28Cr-6Mo samples were approximately 275 ± 13 HB and 255 ± 20 HB detected. In addition, the corrosion properties of the samples were examined by hot corrosion tests at 800, 900 and 1000°C for 165 hours (15 cycles) in 25% wt. K2SO4 + 75% wt. Na2SO4 salt medium. Weight changes, microstructure (SEM-EDS) and phase analysis of the samples after corrosion were carried out, and the corrosion properties of NiAl-34Cr alloy were found to be better compared to the Mo-added alloy.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call