Abstract
Silicon oxide thin film grown at low temperatures (<300–500 °C) is essential for a range of applications in semiconductor devices. In this study, silicon oxide films were deposited at a substrate temperature of ∼300 °C by an atomic layer deposition (ALD) process using Bis(ethyl-methyl-amino)silane (BEMAS). BEMAS precursors adsorbed on the growing surface reacted with ozone but not with H2O. This suggests that the Si–H bonds in the BEMAS precursors adsorbed on the surface are robust and could be cleaved only by ozone. The reaction using BEMAS and ozone exhibited ALD saturation behavior. The dielectric constant of the ALD-SiO2 was measured to be ∼9, which is 2.3 times higher than that (∼3.9) of normal amorphous SiO2. This was attributed to the existence of the ∼10% OH species in the film.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of Vacuum Science & Technology A: Vacuum, Surfaces, and Films
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.