Abstract
To clarify the effect of hydrogen gas on fretting fatigue strength of the materials, which supposed to be used for hydrogen utilization machines, fretting fatigue tests were conducted in hydrogen gas. It is important to take fretting fatigue into account in strength design, because many fatigue failure accidents have occurred at joints or contact parts between components. As a part of the experiments, an austenitic stainless steel was focused in this paper. The material was SUS 304. Fretting fatigue strength in hydrogen gas decreased compared with that in air. Tangential force coefficient increased in the reverse order of fretting fatigue strength. Therefore, one of the reasons of the decrease of fretting fatigue strength was that tangential force was different depending on the environment. Absorption of hydrogen occurred during fretting in hydrogen gas was detected. The absorption could be considered as one of the causes of the decrease of fretting fatigue strength, since fretting fatigue life of pre-charged specimen was decreased and also the crack propagation threshold of short fatigue crack was reduced by hydrogen charge.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call