Abstract
The field electron emission from carbon nanotube films on polycrystalline diamond films was investigated. The carbon nanotubes and diamond films on Si substrates were prepared by a conventional hot filament chemical vapour deposition. The films obtained were characterized by scanning electron microscopy and Raman spectroscopy. The field emission properties of the samples were measured in an ion-pumped vacuum chamber at a pressure of 10-6 Pa.. The experimental results showed that the field emission behaviours of carbon nanotubes/diomond films structure have greatly been improved as compared with carbon nanotubes and diamond films, respectively. A turn-on field of 1.0 V/µm and a maximum current of 500 µA at 1.5 V/µm were observed, which were lower than those of carbon nanotubes and polycrystalline diamond films, respectively. This improvement was attributed to the tip shape of sample surface, which provided an additional local increase in electric field at the tube ends.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.