Abstract
An alumina foam with two kinds of pores was prepared by combining the sponge method and the pore-former method. The large pores were provided by the sponge method, and their sizes were in the range of 1–2 mm. The small pores were produced by the pore-former method with size in the micrometer range. The large pores offered a high porosity while the small pores offered a large surface area. The strength of samples sintered at different temperatures was measured, and the effect of sintering temperature on foam strength was analyzed by discussing porosity and grain bonding area. The sample sintered at 1550 °C has a compressive strength of 1.3 MPa and a porosity of 86%.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.