Fabrication, characterization and properties of silver nanoparticles using poly (MAA)–chitosan graft copolymer as an ecofriendly non-fibrous textile

Abstract

PurposeThis study aims to address a comprehensive and integrated investigations pertaining to the preparation of AgNPs with well-defined nano-sized scale using the aforementioned poly (meth acrylic acid [MAA])–chitosan graft copolymer, which is cheap, nontoxic, biodegradable and biocompatible agent as a substitute for the traditionally used toxic reducing agents.Design/methodology/approachAgNPs are prepared under a range of conditions, containing silver nitrate and poly (MAA)–chitosan graft copolymer concentrations, time, temperature and pH of the preparation medium. To classify AgNPs obtained under the various conditions, ultraviolet–visible spectroscopy spectra and transmission electron microscopy images are used for characterization of AgNPs instrumentally in addition to the visual color change throughout the work. The work was further extended to study the application of the so prepared AgNPs on cotton fabric to see their suitability as antibacterial agent as well as their durability after certain washing cycles.FindingsAccording to the current investigation, the optimal conditions for AgNPs formation of nearly 3–15 nm in size are 5 g/l, poly (MAA)–chitosan graft copolymer and 300 ppm AgNO3 in addition to carrying out the reaction at 60°C for 30 min at pH 12. Besides, the application of the so prepared AgNPs on cotton fabric displayed a substantial reduction in antibacterial efficiency against gram-positive and gram-negative bacteria estimated even after 10 washing cycles in comparison with untreated one.Originality/valueTo the best of the authors’ information, no comprehensive study of the synthesis of AgNPs using poly (MAA)–chitosan graft copolymer with a graft yield of 48% has been identified in the literature.