Abstract
Hot-electron bolometer mixers employing thin films of conventional superconducting materials have already been successfully fabricated in the past. Magnesium diboride (MgB <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> ) is a promising alternative to conventional superconductors, and we report the fabrication and study of ultrathin MgB <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> films of down to 10 nm deposited by hybrid physical-chemical vapor deposition technique. The MgB <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> films showed T <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">c</sub> of above 36 K, while residual resistivities of up to 26 μΩ · cm were achieved. Critical currents of more than 6 × 10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">6</sup> A · cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-2</sup> at 20 K have been measured for the films with thicknesses ranging from 10 to 100 nm. Fishtail structures have been observed in the magnetic field dependence of the critical current density for the thinnest of these films, indicating the presence of defects, which act as vortex pinning centers. From the magnetic field dependence, an average distance between adjacent pinning centers of 35 nm has been obtained for the thinnest films.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.