Abstract
Ti6Al4V (Ti64) plate was fabricated from powders in vacuum at 10−2 Pa by selective laser melting (SLM) method with single mode fiber laser. Ti64 has a crystal orientation of alpha α + β type. In order to investigate the crystal orientation, a X-ray diffraction in continuous scanning mode and an energy dispersive X-ray spectroscopy were conducted. From the results, it can be found that at the powder, the peak of α (1011), α (0002), α (1010) and α(1012) crystal orientations is detected to be composed mainly of martensitic alpha. Diffraction peaks corresponding to β(110) were detected in vacuum SLM processed samples.Ti6Al4V (Ti64) plate was fabricated from powders in vacuum at 10−2 Pa by selective laser melting (SLM) method with single mode fiber laser. Ti64 has a crystal orientation of alpha α + β type. In order to investigate the crystal orientation, a X-ray diffraction in continuous scanning mode and an energy dispersive X-ray spectroscopy were conducted. From the results, it can be found that at the powder, the peak of α (1011), α (0002), α (1010) and α(1012) crystal orientations is detected to be composed mainly of martensitic alpha. Diffraction peaks corresponding to β(110) were detected in vacuum SLM processed samples.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.