Ethanol electrooxidation in alkaline medium on electrochemically synthesized Co(OH)2/Au composite

Abstract

Gold (Au), cobalt hydroxide (Co(OH)2) and different Co(OH)2/Au compositions were electro-deposited onto stainless steel by a potentiodynamic method from the respective metal-ion solutions. The deposits were characterized by x-ray diffraction (XRD), scanning electron microscope (SEM) and Fourier transformed infra-red spectroscopy (FT-IR). The XRD and IR data confirmed that the deposits were Au, α-Co(OH)2 or Co(OH)2/Au composites. The SEM observations confirmed that the morphology of the Au was spherical, while the α-Co(OH)2 was flakey with pores. The morphology of the Co(OH)2/Au composites consisted of highly agglomerated Au grains distributed on the Co(OH)2 matrix. The electrocatalytic activity of each of the Au, Co(OH)2 and Co(OH)2/Au-composite electrodes towards ethanol electrooxidation in an alkaline medium was investigated by cyclic voltammetry and chronoamperometry. It turned out that the Co(OH)2/Au-composite electrodes exhibited superior catalytic activity for ethanol electrooxidation compared with the pristine Au or Co(OH)2 electrodes. A peak current density as high as 25 mA cm−2 was exhibited by the Co(OH)2/ Au composite while the Au and Co(OH)2 showed only 0.9 and 13 mA cm−2, respectively. The enhanced conductivity of the Co(OH)2/Au matrix due to the presence of Au, as well as the combined catalytic activity, seemed to be responsible for the superior performance of the Co(OH)2/Au-composite electrodes.