Abstract
Ethanol electro-oxidation reaction was investigated considering conventional electrochemical experiments in alkaline media, direct ethanol fuel cell (DEFC), and in situ ATR-FTIR. The working electrode/anodes were composed of monometallic Pt/C, Au/C, Ir/C, and trimetallic PtAuIr/C nanoparticles with atomic Pt/Au/Ir ratios of 40:50:10, 50:40:10, 60:30:10, 70:20:10, and 80:10:10. X-ray diffraction (XRD) suggests PtAuIr/C alloy formation, and according to transmission electron micrographs, the mean particle sizes are from 4 to 6 nm for all catalyst compositions. PtAuIr/C 40:50:10 showed the highest catalytic activity for ethanol electro-oxidation in the electrochemical experiments; using this material, the peak current density from ethanol electro-oxidation on cyclic voltammetry experiment was 50 mA per g of Pt, 3.5 times higher than that observed with Pt/C. The fuel cell performance was superior using all PtAuIr/C compositions than using Pt/C. Au/C and Ir/C presented very poor catalytic activity toward ethanol electro-oxidation. The improved results obtained using PtAuIr/C might be related to the OHads species formed at low overpotential on Ir and to the decrease on adsorption energy of poisoning intermediates on Pt sites, promoted by Au.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.