Epitaxial Growth and Thermal Stability of CoSi2 Layer on (100) Si from Co-C Films without Capping Layer

Abstract

AbstractA uniform epitaxial CoSi2 layer was grown on (100) Si substrate by rapid thermal annealing at 800°C in N2 ambient without capping layers from an amorphous cobalt-carbon film. The amorphous cobalt-carbon film was deposited on Si substrate by the pyrolysis of cyclopentadienyl dicarbonyl cobalt. Co(η5-C5H5)(CO)2. at 350°C. The leakage current measured on the junction, fabricated with the epitaxial CoSi2 layer and annealed at 1000°C for 30 s. was as low as that of the as-fabricated junction without silicide. indicating that epitaxial (100) CoSi2 is thermally stable at temperatures even above 1000°C and has a potential applicability to the salicide process in sub-half micron devices.