Abstract
AbstractSelf-aligned silicide (salicide) formation of epitaxial CoSi2, using a Co/Ti bilayer, on linear oxide (SiO2) patterned (100)Si substrate has been investigated. Rapid thermal annealing (RTA) at 550°C resulted in the lateral encroachment of silicide in the Si under the edge of the oxide. After RTA at 900°C, even though an epitaxial CoSi2 layer was formed on the Si substrate, defects such as lateral encroachment and voids were generated under the edge of the oxide. It was found that such defects lead to device failure due to the deterioration of the gate oxide and the shallow junction.