Abstract

In this work, amorphous silicon-germanium (a-SiGe:H) p-i-n single junction solar cells are fabricated using a 40MHz plasma-enhanced chemical vapor deposition system. Their s-curve characteristics were observed by current density-voltage measurements. Thermal annealing of cells at 150 °C in a vacuum effectively overcame the s-curve behavior. Additionally, comparing the external quantum efficiency spectra of annealed samples with those of as-deposited samples revealed that the spectral response of annealed cells was higher in the long wavelength range (600~900nm). Raman spectroscopy and electrical conductivity analyses revealed that the n-type microcrystalline silicon (n-μc-Si:H) layers of as-deposited cells were not optimal. Experimental results indicate that the i/n barrier heights of the as-deposited and annealed samples were 0.31eV and 0.20eV , respectively. The high energy barrier implies that the bad collection ability of charge carriers near the i/n interfaces of solar cells. An energy conversion efficiency of 6.38% was achieved after post-deposition annealing. The improvement in efficiency is concluded to have been caused largely by retention of n-μc-Si:H layers of high crystallinity and electrical conductivity after annealing.

Full Text
Published version (Free)

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call