Abstract
This study investigates the impact of multi-step austenitization heat treatment on the in-service life of modified AISI A8 cold work tool steel knives used in wood cutting. The knives were subjected to two treatment methods: single quenching and double tempering (SQDT) and double quenching and double tempering (DQDT). Both treatments were followed by physical vapor deposition (PVD) coating to enhance surface properties. The DQDT treatment resulted in a finer microstructure and more uniform carbide distribution. Field tests on 24 knives over 124 h demonstrated up to 130% improvement in wear resistance for DQDT knives, along with superior edge stability and better PVD coating preservation. DQDT knives exhibited ductile fractures characterized by dimples, contrasting with the brittle fracture and cleavage facets in SQDT knives. Residual stress measurements showed higher compressive stresses in DQDT knives (-280 MPa) compared to SQDT knives (-30 MPa), which increased further after field testing. The enhanced performance of DQDT knives is attributed to their refined microstructure, improved carbide distribution, and higher compressive residual stresses, offering significant potential for improving wood cutting tool efficiency and durability.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.