Abstract
YPO4: Tm, Yb inverse opal photonic crystals were successfully synthesized by the colloidal crystal templates method, and the visible-infrared quantum cutting (QC) photoluminescence properties of YPO4: Tm, Yb inverse opal photonic crystals were investigated. We obtained tetragonal phase YPO4 in all the samples when the samples sintered at 950°C for 5 h. The visible emission intensity of Tm3+ decreased significantly when the photonic bandgap was located at 650 nm under 480 nm excitation. On the contrary, the QC emission intensity of Yb3+ was enhanced as compared with the no photonic bandgap sample. When the photonic bandgap was located at 480 nm, the Yb3+ and Tm3+ light-emitting intensity weakened at the same time. We demonstrated that the energy transfer between Tm3+ and Yb3+ is enhanced by the suppression of the red emission of Tm3+. Additionally, the mechanisms for the influence of the photonic bandgap on the energy transfer process of the Tm3+, Yb3+ codoped YPO4 inverse opal are discussed.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call