Abstract
In the present work, we investigated the effect of BiZn0.5Ti0.5O3 composition on energy storage and electrocaloric properties of lead free (1-x)(0.6Ba(Zr0.2Ti0.8)O3‐0.4(Ba0.7Ca0.3)TiO3)–xBiZn0.5Ti0.5O3 [BZCT-BZ] ceramics by varying the x from 0 to 10%. The x-ray diffraction (XRD) analysis evidences the formation of BZCT-BZ solid solution without any secondary or impurity phase. The peaks splitting at 2θ = ∼ 45° and 66° suggested the co-existence of rhombohedral (R) and tetragonal (T) phases (morphotropic phase boundary) at room temperature for x ≤ 1%. Further, BZCT-BZ ceramics with x > 1% exhibited pseudocubic nature. The ferroelectric hysteresis loop confirms relaxor behavior and the decrease in remanent polarization with increase of BZ content is explained based on the back switching calculations. The BZCT-BZ ceramics as function of BZ composition gave the optimum recoverable energy density of 197 mJ/cm3 and an efficiency of 92% at an applied field of 45 kVcm−1. Such an exceptionally high energy storage efficiency is attributed to the enhanced relaxor behavior and superior back switching capability. Further, the values of electrocaloric temperature change and responsivity are found to be 0.67 K at 45 kV/cm and 0.014 Kcm/kV respectively in 0.98BZCT-0.02BZ ceramics. Thus, BZCT-BZ ceramics are appealing candidates for energy storage and electrocaloric application.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.