Abstract
A high temperature micro-impact test has been developed to assess the fracture resistance of hard coatings under repetitive dynamic high strain rate loading at elevated temperatures. The test was used to study the temperature dependence of the resistance to micro-scale impact fatigue of TiAlSiN coatings on cemented carbide at 25–600 °C. Nanoindentation and micro-scratch tests were also performed over the same temperature range. The results of the micro-impact tests were dependent on the impact load, coating microstructure, coating and substrate mechanical properties, and their temperature dependence. At higher temperatures there was a change in failure mechanism from fracture-dominated to plasticity-dominated behaviour under the cyclic loading conditions. This was attributed to coating and substrate softening.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.