Abstract
Vacancy-type defects in GaN with different carbon concentrations ([C]=2×1016−1×1018cm−3) were probed using monoenergetic positron beams. 1.5-μm-thick GaN layers were grown on Si substrates by metalorganic vapor phase epitaxy. Measurements of Doppler broadening spectra and positron lifetimes indicated that the major defect species in the GaN layers was a Ga vacancy coupled with nitrogen vacancies. The positron trapping rate of the defects decreased with increasing [C], which was attributed to the downward shift of the Fermi level position due to C acceptor and the resultant change in the defect charge state (neutral to positive). Under illumination, the defect charge state was changed from positive to neutral, which was attributed to the trapping of the excited electrons by the defects (V++e−→V0). The effect of illumination was suppressed for the GaN layer with [C]≥1018cm−3, which was ascribed to the excellent electron trapping property of C in GaN.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.