Abstract
Though the classical transport theory does not mathematically express the Arrhenius-like relation between Cr-loss flux due to volatilisation and absolute temperature, such relation was experimentally observed for 409L stainless steel exposed at 600–750 °C. Volatilisation calculation in the present cases can be estimated giving such relation because of the nearly linear relation between mass transfer coefficient and temperature. Cr-loss fluxes in O2 with 20 and 40 % H2O are close to or coincided with the fluxes calculated from MnCr2O4 evaporation. Increasing water vapour could enhance volatilisation contributed from the raised CrO2(OH)2 pressure, reduce oxidation rate, and worsen scale adhesion.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.