Abstract
The oxidation of ferritic stainless steels has been studied under solid oxide fuel cell (SOFC) interconnect “dual” exposure conditions, i.e., simultaneous exposure to air on one side of the sample, and fuel (hydrogen) on the other. It was found that, under the dual exposures, the oxidation behavior of the stainless steels at the airside differed significantly from that observed during exposure to air at both sides. Increased water vapor partial pressure in the air at the airside further accelerated the anomalous oxidation, resulting in nucleation and growth of hematite in the scale that led to a localized attack. The accelerated oxidation and growth of the hematite nodules was a result of combined effects of hydrogen transport from the fuel side to the airside and the presence of increased water vapor.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.