Abstract
Abstract Ba(Co1/3Nb2/3)O3(BCN) has a 1:2 ordered hexagonal structure. A large amount of the liquid phase, which contains high concentrations of Ba and Nb ions was found in the BCN ceramics. Q-values of BCN increased with increasing sintering temperature; however, it significantly decreased when the sintering temperature exceeded 1400 °C. The presence of a large amount of liquid phase could be responsible for the decrease of the Q-value. For (1−x)Ba(Co1/3Nb2/3)O3–xBa(Zn1/3Nb2/3)O3 [(1−x)BCN–xBZN] ceramics, the 1:2 ordered hexagonal structure was observed in the specimens with x⩽0.3 and the BaNb6O16 second phase was found in the specimens with x⩾0.6. Grain growth, which is related to the BaNb6O16 second phase occurred in the specimens with x⩾0.5. In this work, the excellent microwave dielectric properties of τf=0.0 ppm/°C, er=34.5 and Q×f=97,000 GHz were obtained for the 0.7BCN–0.3BZN ceramics sintered at 1400 °C for 20 h.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call