Abstract
The effects of MnO2 addition on k31 and Qm were investigated for Pb(Zr0.5Ti0.5)O3(PZT). The MnO2 addition increased Qm and k31 in a low poling field. This result indicated that Mn-doped PZT possessed properties of `soft' and `hard' piezoelectrics simultaneously. Electron spin resonance measurement indicated that Mn2+, Mn3+ and Mn4+ coexisted in PZT. The tetragonality of the PZT lattice and the Curie temperature decreased with MnO2 content. From these results, it was found that the increase in k31 of Mn-doped PZT was due to the change of the crystal structure toward a cubic system, and the increase in Qm to Mn2+ and Mn3+ ions working as acceptor dopants. The characteristic feature of Mn is that its addition to PZT decreases tetragonality, and various valence states coexist in proper ratio in Mn-doped PZT sintered in atmosphere.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.