Abstract
This paper presents an experimental study on the effects of elevated temperature and water quenching on compressive strength and microstructure of ultra-high performance concrete (UHPC) containing polypropylene (PP) fiber, steel fiber, and larger aggregates. UHPC samples were exposed to elevated temperature up to 900 °C. The residual strengths of the samples were measured after furnace cooling or immediate quenching in water. Microstructures and phase change of UHPCs were investigated by using X-ray Diffraction (XRD) and Field Emission Scanning Electron Microscope (FESEM). Test results show that the compressive strength increased significantly after exposure to 300 °C due to further hydration of unhydrated cement clinkers but start to decrease sharply after 600 °C exposure due to decomposition of hydration products. Steel fiber had beneficial effect, but PP fiber and larger aggregate reduced the compressive strength of UHPC because they promoted damage at micro scale. Water quenching decreased compressive strength significantly for all exposure temperatures. This reduction is mainly attributed to the formation of microcracks caused by high thermal stress.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.