Effect of toothbrushing on titanium surface: An approach to understanding surface properties of brushed titanium

Abstract

Summary Objectives This in vitro study aimed to characterize the surface morphology and composition of toothbrushed titanium casting and thereby to elucidate interactions between the metal and abrasive material in dentifrice. Methods Specimens were cast from CP Ti ingots and then mirror-finished. Two fluoride-free toothpastes containing crystalline CaHPO 4 ·2H 2 O and amorphous SiO 2 particles as abrasive were slurried with distilled water (15 g/30 mL). While toothbrushes were reciprocated at 120 strokes/min for 350,400 strokes, the specimens were brushed with the respective slurries under a load of 2.45 N. The brushed and non-brushed surfaces were characterized by means of SPM, EPMA, and XPS. SPM data were analyzed using one-way ANOVA, followed by post hoc Tukey test ( p Results Irrespective of toothpastes, toothbrushing had a significant influence on surface roughness. The CaHPO 4 ·2H 2 O-containing paste produced much rougher surface than the SiO 2 -containing paste. Both the surfaces were chemically altered due to reactions with the respective abrasive materials. Abrading chips had dimensions of micron to submicron order. A number of chips were attached to abrasive particles. Significance The alterations of surface morphology and composition may affect biological responses of titanium in the oral environment. Dentifrice with lower abrasivity might be advisable for daily oral hygiene practice of patients with dental titanium devices.