Abstract
La1-xSrxMnO3 (x = 0.1, 0.2, and 0.3) nanoparticles (LSMO NPs) were successfully synthesized by a simple sonochemical-assisted method. The prepared samples were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The compositions of samples were determined by energy-dispersive spectroscopy (EDS) analysis. The temperature dependence of the resistivity of samples was measured using four-probe technique, and the magnetic measurement was performed in a Magnetic Property Measurement System (MPMS XL 7.0). SEM, TEM, and XRD show that LSMO NPs are 40∼80 nm in diameter with a very clean surface, and exhibit single phase perovskite structure. The ferromagnetic transition temperature (Tc) and metal-insulator transition temperature (Tp) of the NPs increase with the doping level x. The maximum values of Tc (377 K) and Tp (264 K) occur at x = 0.3. In this work, the effect of strontium doping level on electrical transport and magnetic properties was systematically studied.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.