Abstract
Tin sulfate (SnSO4) can change the setting time and strength of cement due to the presence of sulfate (SO42−), and can reduce the content of hexavalent chromium (Cr6+) in cement owing to its strong reduction ability. This paper studies the influence of stannous sulfate on physical and chemical properties of cement under different temperature and humidity conditions. Adding SnSO4 to the cement mixer resulted in formation of calcium hydroxo-tin, (Sn6O4(OH)4) and CaSn(OH)4. The setting time and strength of cement are obviously enhanced by the addition of stannous sulfate than that of gypsum (CaSO4·2H2O) and stannous chloride (SnCl2), which can be attributed to the coupling of sulfate and stannous ions; Compared with gypsum (CaSO4·2H2O), SnSO4 could hardly produce delayed ettringite (60 days) under hot temperature curing conditions; and water conservation may ensure the full use of stannous sulfate in cement. The total reducing capacity of the SnSO4 on hexavalent chromium (Cr6+) may decrease under hot temperature, but its reduction capacity is still higher than that of ferrous sulfate (FeSO4) under the same conditions. Results from SEM showed that SnSO4 was incorporated into the hydrated cement matrix.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.