Abstract
P-i-n structures with SiO2/nc-Si/SiO2 multilayers as intrinsic layer were prepared in conventional plasma enhanced chemical vapor deposition system. Their carrier transport and electroluminescence properties were investigated. Two resonant tunneling related current peaks with current dropping gradually under forward bias were observed in the current voltage curve. Non-uniformity of the interfaces might be responsible for the gradual dropping of the current. Electroluminescence intensity of the device under bias of 7V which is near the resonant tunneling peak voltage of 7.2V was weaker than that under 6.5V. According to the Gaussian fitting results of the spectra, the intensity of the sub-peak of 650nm originating from recombination of injected electrons and holes was decreased the most. When resonant tunneling conditions are met, it might be that most of the injected electrons participate in resonant tunneling and fewer in Pool–Frenkel tunneling, which is the main carrier transport mechanism, to contribute to electroluminescence intensity.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.