Abstract
Environmental concerns have prompted researchers to focus on the development of alternative building materials like geopolymer concrete. However, their implementation requires curing beyond 60°C, which limits their application on building sites. This study aims to design a geopolymer concrete at room temperature (30 ± 5°C) in a laboratory in Burkina Faso using a metakaolin-based geopolymer binder activated by an alkaline solution of NaOH and natural aggregates. Portland cement type CEM I 42.5 was used by mass substitution (0 to 25%) of metakaolin to promote curing at ambient temperature. The samples were cured for 7 to 28 days and characterized for physical, mechanical, and durability properties. The results showed that the incorporation of 0 to 20% cement significantly improved the compressive strength from 9.9 to 30.5 MPa and the tensile strength from 1.2 to 2.2 MPa. However, Portland cement has various effects on the durability of geopolymer concrete. It reduces the porosity accessible by water from 15 to 13% and decreases the resistance to acid attack by increasing the mass loss from 2 to 7%. This confirms that common concrete types C20/25 or C25/30 can be casted using geopolymer concrete on the sites in Burkina Faso once their durability is confirmed. Doi: 10.28991/CEJ-2023-09-07-04 Full Text: PDF
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.