Abstract
In this study, the effects of polystyrene (PS) latex addition on the particle morphology and the pore content of calcium oxide (CaO) were investigated. The CaO particles were prepared using an ultrasonic nebulizer-assisted spray-pyrolysis method with variation of the PS/Ca(NO 3 ) 2 ·4H 2 O mass ratio in the precursor. Good crystallinity of CaO was obtained at 825°C of synthesis temperature under 2 l/min of nitrogen gas flow, which was confirmed by Fourier transform infrared (FTIR) spectroscopy and X-ray diffraction (XRD). According to scanning electron microscope (SEM) characterization, the CaO particles synthesized with 0 and 25 wt% PS addition had an almost spherical shape with an average size of 1.58 and 1.48 µm, respectively. In addition, macropores were formed in the CaO particles prepared with 25 wt% PS addition that had an average pore diameter of 583.26 nm. Meanwhile, the CaO particles prepared with 75 wt% PS addition had a random shape and an average size of 1.41 µm. The mesopore content was investigated by Barret-Joyner-Halenda (BJH) analysis, which showed improvement of the pore size from 3.45 nm to 5.42 nm for 0 and 25 wt% PS addition, respectively, which is proportional to the pore volume, pore surface area, and the capacity of SO 2 retention.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.