Abstract
SIMP steel is newly developed fully martensitic steel for lead-cooled fast reactors and accelerator-driven systems. It is important to evaluate its radiation resistance via high flux neutron irradiation, where dense He atoms can be formed via (n, α) transmutation reaction. Co-irradiation with Fe and He ions, instead of neutron, was performed. Specimens were irradiated with 6.4-MeV Fe ions to the damage dose of 5 dpa at a depth of 600 nm. Three different helium injection ratios of 60-appm He/dpa (dpa: displacements per atom), 200-appm He/dpa and 600-appm He/dpa at a depth of 600 nm, were performed. Two different irradiation temperatures of 300 °C and 450 °C were carried out. The effect of helium concentration on the microstructure of Fe-irradiated SIMP steel was investigated. Microstructural damage was observed using transmission electron microscopy. The formed dislocation loops and bubbles depended on the helium injection ratio and irradiation temperature. Lots of dislocation loops and helium bubbles were homogeneously distributed at 300 °C, but not at 450 °C. The causes of observed effects are discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.