Abstract
A type of home-made reduced activation martensitic steel, high silicon (SIMP) steel, is homogeneously irradiated with energetic Fe ions to the doses of 0.1, 0.25 and 1 displacement per atom (dpa), respectively, at 300°C and 1 dpa, at 400°C. Microstructural changes are investigated in detail by transmission electron microscopy with cross-section technique. Interstitial defects and defect clusters induced by Fe-ion irradiation are observed in all the specimens under different conditions. It is found that with increasing irradiation temperature, size of defect clusters increases while the density drops quickly. The results of element chemical mapping from the STEM images indicate that the Si element enrichment and Ta element depletion occur inside the precipitates in the matrix of SIMP steel irradiated to a dose of 1 dpa at 300°C. Correlations between the microstructure and irradiation conditions are briefly discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.