Abstract
Volatility of Cs from borosilicate glasses incorporated with different additives like ZnO, BaO, and CaO have been investigated as a function of heating temperatures (900°C, 950°C, and 1000°C) and time. According to the lower Cs volatility, the sequence of the incorporated oxides is arrived as ZnO < B2O3 < BaO < CaO. It is confirmed that the volatilization of Cs occurred predominantly through diffusion controlled process. From the temperature‐dependence volatility profiles of Cs, the activation energy and frequency factor was calculated and found to be in the range of 300–500 kJ/mol and 103–1012 cm2/s, lowest for ZnO and highest for CaO containing glasses. It was found that the frequency factor and not the activation energy were controlling the Cs loss. The observed variations in the activation energy and frequency factor have been explained by a unique model structure and possible interactions of Cs with different structural units formed due to incorporation of the different additives.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.