Abstract
Magnesium-based metal glasses (MMGs) have broad application potential as bio-implant materials because of their disordered atomic structure, fine degradability, low elasticity modulus, and high strength. However, their low plasticity and poor corrosion resistance limit their application. In the present study, Mg-Zn-Yb-Ag metallic glasses were fabricated by injecting into a copper roller. The addition of trace amounts of ytterbium (Yb) and precious metal silver significantly improved the ductility of MMGs under bending and tensile loading. The results show that the amorphous alloy with 4 at% of Yb exhibits optimum specific strength mainly because of high-density coarsening shear bands. Electrochemical experiments, immersion test, and analysis of corrosion products by XPS and EDS after immersion showed that the amorphous alloy with 4 at% of Yb exhibits the greatest corrosion resistance among the four samples because of rare earth (Yb) oxide film. The addition of the appropriate amount of the rare-earth element Yb to amorphous Mg-based alloys can not only remarkably influence the alloy plasticity but also improve the alloy corrosion resistance, thereby increasing the alloy application prospects.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.