Abstract
In this study, we report on investigation of the electrocaloric (EC) effect in lead-free Ba(SnxTi1-x)O3 (BSnT) ceramics with compositions in the range of 0.08 ≤ x ≤ 0.15 by the direct measurement method using a differential scanning calorimeter. The maximum EC temperature change, ΔTEC-max = 0.63 K under an electric field of 2 kV/mm, was observed for the composition with x = 0.11 at ∼44 °C around the multiphase coexistence region. We observed that the EC effect also peaks at transitions between ferroelectric phases of different symmetries. Comparison with the results of indirect EC measurements from our previous work shows that the indirect approach provides reasonable estimations of the magnitude of the largest EC temperature changes and EC strength. However, it fails to describe correctly temperature dependences of the EC effect for the compositions showing relaxor-like behaviour (x = 0.14 and 0.15) because of their non-ergodic nature. Our study provides strong evidence supporting that looking for multiphase ferroelectric materials can be very useful to optimize EC performance.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.