Abstract
Nanocrystalline Selenium was synthesized within a silica matrix using a sol-gel method with high-purity SeO2, ethyl alcohol, distilled water, and TEOS (Tetraethyl orthosilicate). This process encapsulated the selenium dioxide in the silica matrix, which was then reduced at about 100°C using an oil bath. Three reducing agents were employed: acetone vapor, and sodium borohydride (NaBH4) and hydrazine (N2H4) in liquid form. DSC-TGA analyses of the precursor mixture determined the crystallization temperature for selenium nanoparticle formation within the matrix to be around 100°C. Post-heating phase analysis via XRD revealed hexagonal structures, with crystallite sizes between 33 and 43 nm determined using Debye-Scherrer's formula. Morphological studies showed irregular polygonal shapes with rough surfaces, with particulate sizes under 0.2µ for acetone vapor, around 0.1µ for hydrazine, and slightly over 0.1µ for sodium borohydride. Time variations were explored to observe phase and crystallite size changes. FTIR analysis was conducted for bonding assessment, revealing M-O coordination. The composite's absorbance was examined through UV-VIS spectroscopy, and its morphological attributes were investigated using FESEM analysis, complemented by EDX to determine elemental composition
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.