Abstract
In this study, an experimental program was conducted to investigate the effect of microwave curing on the strength of geopolymer. Volumetric heating provided by microwave curing results in faster strength development as compared to conventional heat curing that depends on heat transmission from the outside to the core of a specimen. Initially, the effect of different traditional curing methods (ambient air, water, and oven) on the strength development of Class F fly ash activated by sodium silicate and sodium hydroxide was investigated. Later, microwave curing and oven curing were introduced at higher temperatures in short periods of time (≤ 60 min) as alternative curing methods. Results showed that the compressive strength of geopolymer pastes cured in a microwave oven was superior to those of the control cured in a conventional oven at 90 and 120 °C for the same period. When the size of specimen size reduced from 50 mm to 25mm, the strength development rate of the geopolymer decreased as the microwave curing time increased. A 56 MPa compressive strength was obtained for 25 mm size geopolymer paste cured in a microwave oven for five minutes.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.