Abstract

Geopolymer cement (GPC) is made from aluminum and silicon, instead of calcium and silicon(OPC). Geopolymer are a type of inorganic polymer that can be formed at room temperature byusing industrial waste (waste materials) such as ground granulated blast-furnace slag (GGBFS),Metakilon (MK) and Red mud (RD) or by products as source materials to form a solid binderthat looks like and performs a similar function to OPC. Geopolymer concrete gets advantagespecification in resistivity to highly aggressive media and the resistivity to change inmechanical and physical characterization at high temperature compared to the traditionalconcrete. this paper mainly study the preparation of Geopolymer cement to using in concreteinstead of Portland cement and discuss the effect different factors on the compressive strengthof Geopolymer paste without natural and chemicals additive (the effect ratio of (slag ,Metakilon, Red mud , sodium hydroxide and sodium silicate) Four parameters were studied.The first parameter, the effect of changing ratio between sodium hydroxide and sodium silicate.NaOH : Na2SiO3 , secondly the effect of changing ratio between slag and Metakilon GGBFS:MK, thirdly the effect of changing ratio between slag and Red mud GGBFS :RM , fourthlythe effect of changing degree curing temperature all samples curing different condition suchas air , water , steam , oven . The results show that get high compressive strength at ratiobetween sodium hydroxide and sodium silicate (NaOH : Na2SiO3), slag and Metakilon(GGBFS :MK) , slag and Red mud ( GGBFS :RM) is 1:2.5 , 0.95:0.05 , 0.90:0.10 respectivelyand the best mix have high compressive strength at various combinations between slag,Metakilon and Red mud by ratio GGBFS : MK : RM is 0.85:0.05:0.10. By inspecting the resultit can be noticed that in case geopolymer concrete the best curing method gives highcompressive strength in oven are compared air, steam, water and steam curing is better than air,water and air curing is better than water curing and the effect temperature curing type oncompressive strength, Regardless of the compressive strength of samples increases with theincrease in curing temperature.

Full Text
Published version (Free)

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call