AbstractThis paper reports the comparative study of the microstructure, melting point, hardness and electrical resistivity of as-cast eutectic Sn-8.8 wt.% Zn, Sn-3.5 wt.% Ag, Sn-43 wt.% Bi and Sn-0.7 wt.% Cu lead-free solder alloys. Sn-3.5 wt.% Ag eutectic solder alloy was found to have the lowest electrical resistivity of 1.91 μΩ · cm whereas the highest electrical resistivity of 14.17 μΩ · cm was observed in the case of Sn-43 wt.% Bi eutectic solder alloy. The lowest melting point of 141.60°C was observed in the case of Sn-43 wt.% Bi eutectic alloy whereas the highest melting point of 243.28°C was observed in the case of Sn-3.5 wt.% Ag solder alloy. The results of the various solder alloys were compared with the properties of commercially available Sn-38.1 wt.% Pb eutectic solder alloy.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.