Deterioration of electromotive force of chromel-alumel thermocouples in reducing atmospheres at high temperatures

Abstract

The deterioration of electromotive force (emf) of Chromel-Alumel (CA) thermocouples in 80 pct H2 + 15 pct CO + 5 pct CO2 has been analyzed in terms of the corrosion behavior of Chromel. Emf of the CA thermocouple deteriorated drastically in 80 pct H2 + 15 pct CO + 5 pct CO2. After exposure for about 1000 hours at 900 °C, the decrease of emf was about 16 mV. The deterioration process could be separated into three terms. The first term, which has the smallest time constant of about 20 hours, was attributed to carbon deposition on the Chromel surface in the temperature range of 600 to 700 °C. The second term, which has a time constant of about 100 hours, was attributed to the severe internal oxidation of chromium in the temperature range of 500 to 800 °C. The third term, having the largest time constant of several thousand hours, might be attributed to the moderate and gradual preferential oxidation of chromium in Chromel in the range 800 to 900 °C. Boron nitride (BN) coating on CA thermocouples could reduce this deterioration of emf; the decrease of emf was improved to about 3 °C during 700 hours test at 900 °C.