Cu Nanoparticles Improved Thermal Property of Form-Stable Phase Change Materials Made with Carbon Nanofibers and LA-MA-SA Eutectic Mixture

Abstract

A novel form-stable phase change materials (FSPCMs) was fabricated by incorporating fatty acid eutectics with electrospun carbon nanofibers (CNFs) surface-attached with copper (Cu) nanoparticles. Three different Cu/CNFs mats were made through combining the technique and principle of electrospinning, pre-oxidation/carbonization and in-situ reduction, while lauric-myristic-stearic acid (LA-MA-SA) ternary eutectic mixture was prepared as the model PCM. The morphology and crystal structure of Cu/CNFs were characterized by Fourier transfer infrared (FT-IR) spectra, Scanning electron microscopy (SEM), X-ray diffraction (XRD) and X-ray energy dispersive spectroscopy (EDS), respectively. The results showed that Cu nanoparticles dispersed uniformly on the surface of CNFs mats without agglomeration, and Cu/CNFs mats could provide the mechanical support for FSPCMs and effectively prevent the flow/leakage of molten fatty acid. Morphological structures, as well as the properties of thermal energy storage and thermal energy storage/retrieval rates, of the resulting FSPCMs were investigated by SEM, Differential scanning calorimetry (DSC), and measurement of melting/freezing times, respectively. The results indicated that the fabricated FSPCMs exhibited desired structural morphology, and LA-MA-SA well dispersed in three-dimensional porous structure of Cu/CNFs mats. The melting and crystallization enthalpies of the fabricated FSPCMs were in the range of 117.1-140.7 kJ/kg and 117.2-142.4 kJ/kg, respectively. In comparison with melting/freezing times of LA-MA-SA ternary eutectic mixture, the melting/freezing times of fabricated FSPCMs were respectively decreased ~27.0-49.2% and ~44.1-63.0%. The fabricated FSPCMs possessed good thermal energy storage/retrieval property, and might have great potential for renewable energy storage applications.