Abstract
The crystallographic dependence of the DC electric (E) field induced strain and phase transition in Na0.5Bi0.5TiO3-5.6%BaTiO3 (NBT-5.6%BT) single crystals has been investigated. An induced transition between pseudocubic and tetragonal structures was observed under E = 10 kV/cm for fields applied along the 〈001〉 direction, whereas an induced transition between pseudocubic and rhombohedral structures was observed when the E-field was applied along 〈111〉. Our results show near the morphotropic phase boundary that the phase stability of NBT-x%BT is dependent on the crystallographic direction along which E was applied.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.