Abstract
Effects of Mn and Cr substitution for Co on crystallographic and magnetic properties of inverse-spinel CoFe 2O 4 thin films were investigated. The crystal structure of the samples remain cubic for x<1 with the lattice constant ( a 0) increasing with x for Mn doping and remaining constant for Cr doping. Tetrahedral Fe 2+ ions were detected in Cr x Co 1− x Fe 2O 4 by Mössbauer spectroscopy while no such ions existed in Mn x Co 1− x Fe 2O 4. The appearance of the tetrahedral Fe 2+ ions can be explained in terms of the Cr 3+ substitution for the octahedral Co 2+ sites with the resultant charge imbalance being compensated by a reduction of the tetrahedral Fe 3+ into Fe 2+. The observed variation in a 0 and magnetic properties can be partly explained in terms of Mn 2+ and Cr 3+ substitution of octahedral sites in Mn x Co 1− x Fe 2O 4 and Cr x Co 1− x Fe 2O 4, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.