Abstract
The crystallization behaviour of as-prepared and nucleated Ge17Sb23Se60 thin films was studied by means of differential scanning calorimetry, X-ray diffraction analysis and scanning electron microscopy. Detailed analysis of the non-isothermal crystal growth kinetics was performed; the apparent activation energy, kinetic model and value of the pre-exponential factor were determined. The kinetic behaviour was found to be surprisingly close to the ideal Johnson–Mehl–Avrami nucleation-growth process, with the only non-ideality being the prolonged peak end tail (which may be a specificity associated with certain thicknesses of thin layers). This corresponds to the initiation of crystal growth in agreement with the classical nucleation theory, with the amount of mechanical defects and strains being negligible. The value of the kinetic parameter suggests two-dimensional crystal growth, which is consistent with the idea of macroscopic crystallites growing in a sterically restricted thin layer. A similar conclusion can be made on the basis of direct microscopic observation of the crystallites’ morphology.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.