The creep anisotropy of Ni-based single crystal superalloys was studied at 750 °C/750 MPa. Transmission electron microscopy (TEM) observations showed that stacking faults and micro-twins were the typical dislocation configurations, which all originated from the activity of {111} 〈112〉 slip systems. Then, the orientation rotation caused by the activity of the main {111} 〈112〉 slip system would accelerate the specimen fracturing in shear fracture mode. Furthermore, the orientation rotation would dominate the creep anisotropy. The orientation rotation would occur during the entire creep process, the greater the degree of rotation, the more severe the asynchrony of rotation, which would result in nonuniform deformation and local stress concentration, and exacerbate the failure of the specimen.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.