Abstract
Achieving intrinsic strengthening of boron nitride nanosheets (BNNSs) in Ti matrix composites was still an unsettled issue due to its severe and uncontrollable interface reaction. In the present study, high-performance BNNSs/Ti composites were fabricated by using the warm compaction (WC) technique and rapid heat treatment (HT) strategy on the basis of interfacial nano-TiBw design. The intrinsic structure of BNNSs was well-retained and nano-TiBw on partially reacted BNNSs led to a brilliant interface bonding and BNNSs intrinsic strengthening. Tensile tests revealed that 0.1 wt.%BNNSs/Ti composites exhibited the tensile strength (UTS) of 876 MPa (61% higher than pure Ti) and the fracture elongation of 22.6%, demonstrating the well-balanced property. By employing the in-situ TEM experiment, we solve an existing debate, uncovering the synergistic toughening effect from BNNSs and interfacial nano-TiBw which effectively inhibited the micro-cracks propagation on BNNSs and heterogeneous interface. This work paves a new way for developing high-performance BNNSs/Ti composites by reaction interface manipulation and underscores the importance of maintaining BNNSs intrinsic structure in the Ti matrix.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.