Abstract
A covalent adaptable network (CAN) of semicrystalline polyolefin blends with triple-shape memory effects was fabricated by the reactive melt blending of maleated polypropylene (mPP) and maleated polyolefin elastomer (mPOE) (50 wt/50 wt) in the presence of a small amount of a tetrafunctional thiol (PETMP) and 1,5,7-triazabicyclo [4,4,0]dec-5-ene (TBD). The polymer blend formed a chemically crosslinked network via the reaction between the thiol group of PETMP and maleic anhydride of both polymers in the blend, which was confirmed by FTIR, the variation of torque during the melt mixing process, a solubility test, and DMA. DSC analysis revealed that the crosslinked polyolefin blends show two distinct crystalline melting transitions corresponding to each component polymer. Improved tensile strength as well as elongation at break were observed in the crosslinked blend as compared to the simple blend, and the mechanical properties were maintained after repeated melt processing. These results suggest that thermoplastic polyolefin blends can be transformed into a high-performance and value-added material with good recyclability and reprocessability.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.