Abstract
AbstractImmersion tests and potentiodynamic polarization measurements were conducted in 1 M sulfuric acid solution (H2SO4) at ambient temperature (∼25 °C) to investigate the corrosion behavior of CuCrFeNiMn alloy system. The results show that the alloys display a good general corrosion resistance that is mainly influenced by the Cu content and elemental segregation degree. The corrosion resistance degrades when increasing Cu content and elemental segregation degree. Among the tested alloys, the CuCr2Fe2Ni2Mn2 alloy with low Cu content and elemental segregation degree displays a better general corrosion resistance. On the contrary, the Cu2CrFe2NiMn2 alloy with high Cu content and elemental segregation degree exhibits the worst general corrosion resistance.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.