Abstract
AbstractThe hot dip aluminized ASTM 1035 steels (Al‐coated steel) underwent anodic oxidization, and various thicknesses of Al2O3 coating were applied to the surface of the Al‐coated steels (Al–Al2O3‐coated steel). The corrosion resistance of the Al–Al2O3‐coated steel was investigated using potentiodynamic tests, electrochemical impedance spectroscopy tests and measurement of galvanic current density in a bimetallic cell. It was found that the anodic oxidation resulted in the formation of a porous Al2O3 coating on the surface of the Al‐coated steel, improving both its corrosion resistance and galvanic corrosion resistance when coupled with carbon fiber reinforced nylon 6 composite (Cf/PA6). Silane treatment effectively sealed the pores within the Al2O3 coating, resulting in improved corrosion protection for Al–Al2O3‐coated steel due to the exceptional insulation, impermeability and hydrophobic properties of silane coating. Compared to the Al‐coated steel/carbon fiber reinforced polymer (CFRP) couple and Al–Al2O3‐coated steel/CFRP couple, stable galvanic current density decreased by approximately 75% and 45%, respectively.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.